  5. 3M™ Dyneon™ Fluoroelastomer FC 1650, 27.5 lb

3M™ Dyneon™ Fluoroelastomer FC 1650, 27.5 lb

3M ID 98021328442
  • Composition: di-polymer of vinylidene fluoride and hexafluoropropylene
  • Medium viscosity gumstock without incorporated curatives
  • Process targets: injection and transfer molding, extrusion, calendering and coatings
  • FC 1650 is amine or bisphenol curable
 More
View all details
Details
  • Composition: di-polymer of vinylidene fluoride and hexafluoropropylene
  • Medium viscosity gumstock without incorporated curatives
  • Process targets: injection and transfer molding, extrusion, calendering and coatings
  • FC 1650 is amine or bisphenol curable

3M™ Dyneon™ Fluoroelastomer FE 5622Q is a Low Viscosity 66 percent Fluorine Copolymer for custom shapes and bonded seals

The "dry" ingredients should be blended before adding to the masticated bum. For best results, Dyneon FC 1650 should be banded on the mill several minutes prior to adding the blended dry ingredients. Once mixed, the compounded stockes have good scorch resistance and storage stability.

Specifications
Brand
Dyneon™
Capabilities
Productivity Improvement
Composition
Dipolymer made from hexafluoropropylene and vinylidene fluoride
Compression Set
15 Percent
Container Type
Box
Cure Technology
Bisphenol
Fluorine Content
65.9 Percent
Industries
Transportation
Mooney Viscosity
47 Mooney Units
Net Weight (Metric)
12.474 kg
Post Cure
24 h @ 260°C
Press Cure
7 min @ 177°C
Product Form
Crumb
Product Type
FKM
Shelf Life
3 Year
Specific Gravity
1.8
Tensile Strength at Break
13.8 MPa (2,000 psi)
Weight (Metric)
12.5 kg